Influence of the Degree of Deacetylation of Chitosan and BMP-2 Concentration on Biocompatibility and Osteogenic Properties of BMP-2/PLA Granule-Loaded Chitosan/β-Glycerophosphate Hydrogels

Compositions based on chitosan/β-glycerophosphate hydrogels with highly porous polylactide granules can be used to obtain moldable bone graft materials that have osteoinductive and osteoconductive properties. To eliminate the influence of such characteristics as chain length, degree of purification, and molecular weight on a designed material, the one-stock chitosan sample was reacetylated to degrees of deacetylation (DD%) of 19.5, 39, 49, 55, and 56. A study of the chitosan/β-glycerophosphate hydrogel with chitosan of a reduced DD% showed that a low degree of deacetylation increased the MSCs (multipotent stromal cells) viability rate in vitro and reduced the leukocyte infiltration in subcutaneous implantation to Wistar rats in vivo. The addition of 12 wt% polylactide granules resulted in optimal composite mechanical and moldable properties, and increased the modulus of elasticity of the hydrogel-based material by approximately 100 times. Excessive filling of the material with PLA (polylactide) granules (more than 20%) led to material destruction at a ~10% strain. Osteoinductive and osteoconductive properties of the chitosan hydrogel-based material with reacetylated chitosan (39 DD%) and highly porous polylactide granules impregnated with BMP-2 (bone morphogenetic protein-2) have been demonstrated in models of orthotopic and ectopic bone formation. When implanted into a critical-size calvarial defect in rats, the optimal concentration of BMP-2 was 10 μg/mL: bone tissue areas filled the entire material’s thickness. Implantation of the material with 50 μg/mL BMP-2 was accompanied with excessive growth of bone tissue and material displacement beyond the defect. Significant osteoinductive and osteoconductive properties of the material with 10 μg/mL of BMP-2 were also shown in subcutaneous implantation.     

Facile non‐lithographic route to highly aligned silica nanopatterns using unidirectionally aligned polystyrene‐block‐polydimethylsiloxane films

Thin films (monolayer and bilayer) of cylinder forming polystyrene‐block‐polydimethylsiloxane (PS‐b‐PDMS) were shear aligned by the swelling and deswelling of a crosslinked PDMS pad that was physically adhered to the film during solvent vapor annealing. The nanostructures formed by self‐assembly were exposed to ultraviolet‐ozone to partially oxidize the PDMS, followed by calcination in air at 500 °C. In this process, the PS segments were fully decomposed, while the PDMS yielded silica nanostructures. The highly aligned PDMS cylinders were thus deposited as silica nanolines on the silicon substrate. Using a bilayer film, the center‐to‐center distance of these features were effectively halved from 38 to 19 nm. Similarly, by sequential shear‐alignment of two distinct layers, a rhombic array of silica nanolines was fabricated. This methodology provides a facile route to fabricating complex topographically patterned nanostructures. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 1058–1064     

离心力场作用下多孔介质中强制对流换热的研究

对离心流化床中空气通过多孔物料层的强制对流换热进行了理论和实验研究。获得了气流和物料间强制对流换热的准则关联式。研究结果表明,在气流速度和温度梯度方向一致的条件下,强制对流换热比通常的边界层强制对流换热有所强化,其换热的准则关联式具有 Nu=CRePr的线性形式。从而验证了改变气流方向和热流密度矢量之间夹角可以强化换热的这一强化传热新原理。     

非晶态合金薄带与膜的巨磁电阻抗效应理论及计算

通过建立具有平面近横向各向异性场的非晶态合金薄带及膜的磁畴结构模型，利用线性化Maxwell方程组及Landau-Lifshitz方程，推出了在高频交变磁场及外加面内轴向直流磁场H_ex作用下的铁磁材料的与取向相关的磁导率表达式，得到了对方位角平均的相对磁导率及阻抗的计算式，导出了磁导率与张量磁化率分量间的关系，对材料磁导率的实部及虚部随H_ex的变化进行了计算，并给出了对应的磁谱图.建立的磁导率与外磁场的理论关系可将Panina及Kraus给出的理论结果统一起来. 关键词： 非晶态合金薄带及膜 取向相关磁导率 GMI效应理论与计算 近横向各向异性场     

稀掺杂GaNxAs1－x(x≤0.03)薄膜的调制光谱研究

利用室温下压电调制反射光(PzR)谱技术系统测量了N掺杂浓度为0.0%—3%的分子束外延生长GaN_xAs_1-x薄膜，并对图谱中所观察的光学跃迁进行了指认.在GaN_0.005As_0.995和GaN_0.01As_0.99薄膜的PzR谱中观察到此前只在椭圆偏振谱中才看到的N掺杂相关能态E₁+Δ₁+Δ_N.当N掺杂浓度达到 关键词： 压电调制反射光谱(PzR) xAs_1-x薄膜')" href="#">GaN_xAs_1-x薄膜 分子束外延(MBE)     

Roles of SiH4 and SiF4 in growth and structural changes of poly-Si films

The structural properties of polycrystalline silicon films, prepared by plasma enhanced chemical vapor deposition system, with different flow rates of SiH₄/SiF₄ mixtures at 300 °C were investigated. This study indicates that the low hydrogen coverage on the growing surface, under optimum fluorine radicals, will be leaded to an improvement of crystallized area as compared with case of high hydrogen coverage surface. Moreover, the studies of the role of SiH₄ and SiF₄ radicals show that the SiH₄ radicals are important in the nucleation and growth of grains. However, SiF₄ radicals are effective in the structural change of grain boundaries regions and by this way, in the present system, establish the growth of grains under the dominant 〈1 1 0〉 direction. The stress investigation indicates that addition of high flow rate of SiF₄ in amorphous film, results in the nearly stress free films. Finally, we found that the changes in g-value reflect the changes in the intrinsic compressive and tensile stress in the both polycrystalline and amorphous silicon films.     

A study of structural, compositional and optical properties of spray-deposited non-stoichiometric (Zn,Fe)S thin films

Non-stoichiometric ternary chalcogenides (Zn,Fe)S were prepared in the film form by pyrolytic spray deposition technique, using air/nitrogen as the carrier gas. The precursor solution comprised of ZnCl₂, FeCl₂ and thiourea. The depositions were carried out under optimum conditions of experimental parameters viz. carrier gas (air/nitrogen) flow rate, concentration of precursor constituents, nozzle substrate distance and temperature of quartz substrate. The deposited thin films were later sintered in argon at 1073 K for 120 min.The structural, compositional and optical properties of the sintered thin films were studied. X-ray diffraction studies of the thin films indicated the presence of (Zn,Fe)S solid solution with prominent cubic sphalerite phase while surface morphology as determined by scanning electron microscopy (SEM) revealed a granular structure.The chemical composition of the resulting thin films as analyzed by energy dispersive X-ray analysis (EDAX) reflected the composition of the precursor solutions from which the depositions were carried out with Fe at% values ranging from 0.4 up to 33.SEM micrographs of thin films reveal that the grain sizes of the thin films prepared using air as carrier gas and N₂ as carrier gas are in the vicinity of 300 and 150 nm, respectively.The diffuse transmittance measurements for thin films, as a function of wavelength reveal the dependence of direct optical band gap on Fe content and type of phase.     

Electrical properties and Schottky diodes using N-N′diphenyl-1-4phenylenediamine

Thin films of, N-N′diphenyl 1-4phenylene-diamineane are prepared using vacuum sublimation technique. The electrical conductivity from room temperature down to 127 K is studied. It is found that the conduction of charge carriers obeys T^−1/2 dependence on temperature. The average hopping distance, hopping energy, density of states and their variation due to post-deposition heat treatment are studied. Schottky diodes are fabricated with gold as ohmic contact and aluminium as Schottky contact. From the observed current voltage characteristics the saturation current density, diode ideality factor and the barrier height are determined. Their variation with air annealing is also investigated.     

直流磁控溅射一步法原位制备MgB2超导薄膜

用MgB2靶,控制直流磁控溅射工作在异常辉光放电或弧光放电状态,在SrTiO3衬底上原位一次性得到了MgB2超导薄膜,其起始转变温度为32K,零电阻温度为15K. 关键词： 高温超导体 超导薄膜 磁控溅射 二硼化镁     

Studying the process of ionization of hydrogen in conditions of its forced delivery to a porous nickel oxide electrode

The hydrogen ionization process is studied experimentally on an industrial sintered nickel oxide electrode in models of sealed nickel-metal hydride batteries. It is shown that the hydrogen ionization rates that are reached during overcharge by high current densities in conditions of forced gas delivery into the electrode pores (up to 40 mA cm^?2) exceed the self-discharge rate of a nickel-hydrogen battery by two orders of magnitude. Up to 70% of hydrogen delivered into the compact assembly block undergoes ionization during forced charge of models of sealed nickel-metal hydride batteries with a closed hydrogen cycle. Two independent methods (potentiostatic and manometric) are used to determine the relationship between rates of hydrogen ionization with the degree of the electrode filling with gas and perform estimation of the process intensity at a unit reaction surface. It is established that, in conditions of forced gas delivery, practically all the hydrogen oxidation current is generated at the surface of the nickel oxide electrode beneath thin films of an electrolyte solution at the rate of 4–5 mA cm^?2. It is shown that the hydrogen oxidation rate on a nickel oxide electrode filled in part by gas is independent of the electrode potential, probably because of a tangible contribution made by diffusion limitations to the overall hampering of the process.